Model NO.: XG-1K
Width: 1mm
Function: High Strength Fiber
Structure: Synthetic Carbon Chain
Model: Xg-1k
Filament Number: 1k
Linear Density: 120tex
Linear Density of Monofilament: 0.122+/-0.003tex
Linear Density Deviation From Nominal: Max.+/-5%
Tensile Strenght for Single Fiber: Min.58 Cn/Tex
Elongation at Break: 12+/-3%
Oil Content: 1.2+/-0.5%
Humidity: <0.1%
Trademark: XIANGU
Transport Package: Cartons
Specification: ROHS
Origin: Guangdong
HS Code: 5503300000
Model NO.: XG-1K
Width: 1mm
Function: High Strength Fiber
Structure: Synthetic Carbon Chain
Model: Xg-1k
Filament Number: 1k
Linear Density: 120tex
Linear Density of Monofilament: 0.122+/-0.003tex
Linear Density Deviation From Nominal: Max.+/-5%
Tensile Strenght for Single Fiber: Min.58 Cn/Tex
Elongation at Break: 12+/-3%
Oil Content: 1.2+/-0.5%
Humidity: <0.1%
Trademark: XIANGU
Transport Package: Cartons
Specification: ROHS
Origin: Guangdong
HS Code: 5503300000
PAN fiber roving/Polyacrylonitrile precursor is high purity and high strength fiber through wet-two step method with solvent DMF and surface finishing size treatment.It has higher elastic modulus,tensile strength and anti-UV properties,anti-high temperature and cold performance.It is the best raw material of PAN carbon fiber Via Pre-oxidation(200~300ºC),carbonization(1000~1500ºC), Graphitization(2500~3000ºC).

SPECIFICATIONS:
MODEL XG-1K
FILAMENT NUMBER 1K
LINEAR DENSITY 120tex
LINEAR DENSITY
OF MONOFILAMENT		 0.122
±0.003tex
LINEAR DENSITY
DEVIATION FROM NOMINAL		 Max.±5%
TENSILE STRENGHT
FOR SINGLE FIBER		 Min.58 cN/tex
ELONGATION AT BREAK 12±3%
OIL CONTENT 1.2±0.5%
HUMIDITY ≤0.1%


APPLICATION FIELDS:
carbon fiber roving productions or carbon fiber filament manufacturing.
STORAGE:
The polyacrylonitrile precursor should be keep dry in their original cartons and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire

PACKAGING:
1.Inner paper pipe bobbin,net weight 6.00kg.gross weight 7.00kg
2.Carton size:600mm*360mm*190mm,net weight 36.00kg.gross weight 43.00kg.


SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 648 cartons one 20feet container,total net weight is 23328.00kg.
2.transportation by truck:for truck transportation,generally loading in buck with 6layers,about 11664.00kg
3.transportation by rail:for rail transportation,generally loading in buck,about 57600.00kg.   PAN fiber roving/Polyacrylonitrile precursor is high purity and high strength fiber through wet-two step method with solvent DMF and surface finishing size treatment.It has higher elastic modulus,tensile strength and anti-UV properties,anti-high temperature and cold performance.It is the best raw material of PAN carbon fiber Via Pre-oxidation(200~300ºC),carbonization(1000~1500ºC), Graphitization(2500~3000ºC).

SPECIFICATIONS:
MODEL XG-1K
FILAMENT NUMBER 1K
LINEAR DENSITY 120tex
LINEAR DENSITY
OF MONOFILAMENT		 0.122
±0.003tex
LINEAR DENSITY
DEVIATION FROM NOMINAL		 Max.±5%
TENSILE STRENGHT
FOR SINGLE FIBER		 Min.58 cN/tex
ELONGATION AT BREAK 12±3%
OIL CONTENT 1.2±0.5%
HUMIDITY ≤0.1%


APPLICATION FIELDS:
carbon fiber roving productions or carbon fiber filament manufacturing.
STORAGE:
The polyacrylonitrile precursor should be keep dry in their original cartons and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire

PACKAGING:
1.Inner paper pipe bobbin,net weight 6.00kg.gross weight 7.00kg
2.Carton size:600mm*360mm*190mm,net weight 36.00kg.gross weight 43.00kg.


SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 648 cartons one 20feet container,total net weight is 23328.00kg.
2.transportation by truck:for truck transportation,generally loading in buck with 6layers,about 11664.00kg
3.transportation by rail:for rail transportation,generally loading in buck,about 57600.00kg.  

Transparent Black With Stud For Carpet Lip Pvc

Transparent Black With Stud For Carpet Lip Pvc,Waterproof Rug Pad,Waterproof Floor Mat,Waterproof Carpet Pad

Taizhou Ruihu Plastics Co.,Ltd , https://www.tzruihu.com

Posted on